Pure Titanium Wire 2.4mm With Pickling Surface
Erti-5 Titanium Welding Wire is widely used in aerospace, chemical industry, medical treatment, metallurgy, construction and automobile industries, due to its good corrosion resistance, low temperature and high temperature resistance, high strength, small elastic modulus and low density. The density of titanium alloy is generally around 4.51g/cm3, which is only 60% of steel.
Features
Erti-5 Titanium Welding Wire has its surface clean, with no oxidation color, no cracks, peeling, pricking, speckles and inclusions. This wire has good heat resistance, strength, plasticity, toughness, formability, weldability, corrosion resistance and biocompatibility, which is widely used and favored. The amount of this alloy has accounted for 75-85% of all titanium alloys.
Product specification:Diameter: 1.0 mm to 6.0 mm
The material: ERTi-5 Titanium Welding Wire(TC4 Ti-6Al-4V)
| ASTM Base Metal Grade | Base metal | Normal composition | Recommended Filler Metal |
| | UTS(min.) ksi[Mpa] | YS(min.) ksi[Mpa] | | |
| Grade 1 | 35[240] | 20[138] | Unalloyed Ti CP1 | ERTi-1 |
| Grade 2 | 50[345] | 40[275] | Unalloyed Ti CP2 | ERTi-2 |
| Grade 4 | 80[550] | 70[483] | Unalloyed Ti CP4 | ERTi-4 |
| Grade 5 | 130[895] | 120[828] | Ti 6AL-4V | ERTi-5 |
| Grade 7 | 50[345] | 40[275] | Ti 0.15Pd | ERTi-7 |
| AWS | CHEMICAL SPECIFICATIONS |
| AWS A5.16 | UNS | C | O | N | H | I | Al | V | Pd |
| | Number | | | | | | | | |
| ERTi 1 | R50100 | 0.03 | 0.03-0.10 | 0.012 | 0.005 | 0.08 | - | - | - |
| ERTi 2 | R50120 | 0.03 | 0.08-0.16 | 0.015 | 0.008 | 0.12 | - | - | - |
| ERTi 4 | R50130 | 0.03 | 0.08-0.32 | 0.025 | 0.008 | 0.25 | - | - | - |
| ERTi 5 | R56400 | 0.05 | 0.12-0.20 | 0.03 | 0.015 | 0.22 | 5.5-6.7 | 3.5-4.5 | - |
| ERTi 7 | R52401 | 0.03 | 0.08-0.16 | 0.015 | 0.008 | 0.12 | - | - | 0.12-0.25
|
|
|
Straight Pure Titanium Wire Erti-4 With Pickling Surface Images
|